A layered compound-metal particle composite 3 is obtained by the addition, to an organically modified layered compound 1 formed by the intercalation of organic ions between layers of a layered compound, of both an aqueous colloidal metal solution 2 in which metal particles are dispersed as a metal colloid in water, and a nonaqueous solvent which is a poor solvent for the metal colloid and has an excellent ability to swell the organically modified layered compound 1.

A method of photoplating a metal contact onto a surface of a cathode of a photovoltaic device is provided using light induced plating technique. The method comprises: a) immersing the photovoltaic device in a solution of metal ions, where the metal ions are a species which is to be plated onto the surface of the cathode of the photovoltaic device; and b) illuminating the photovoltaic device, using a light source of time varying intensity. This results in nett plating which is faster in a direction normal to the surface of the cathode than in a direction in a plane of the surface of the cathode.

Hemispheres and spheres are formed and employed for a plurality of applications. Hemispheres are employed to form a substrate having an upper surface and a lower surface. The upper surface includes peaks of pillars which have a base attached to the lower surface. The peaks have a density defined at the upper surface by an array of hemispherical metal structures that act as a mask during an etch to remove substrate material down to the lower surface during formation of the pillars. The pillars are dense and uniform and include a microscale average diameter. The spheres are formed as independent metal spheres or nanoparticles for other applications.

A feeding apparatus feeds a metal strip with cutaway portions in a conveying direction and includes: a reference plate on which the metal strip is placed and in which a slit is formed; moving bodies that are provided below the reference plate and are moved by driving means parallel to the reference plate in the conveying direction; feed pins that advance into the cutaway portions, are provided on the moving bodies so as to move up and down with respect to the reference plate, and pull the metal strip in the conveying direction when the moving bodies move; and at least one guide portion that contacts a side surface on an opposite side of the metal strip to the cutaway portions and guides conveyance of the metal strip.

A method of mechanically treating alloy metal surgical needles to improve bending strength is disclosed. The needles are curved and reverse-curved in this method to improve bending strength.

Fluid treatment systems and compositions are provided including (a) at least one material including (1) at least one carboxylic acid functional group and (2) at least one sulfur-containing group selected from the group consisting of sulfonyl functional groups, sulfonate functional groups and mixtures thereof; and (b) at least one friction reducing agent selected from the group consisting of guar gums, polyacrylamides, hydratable cellulosic materials, viscoelastic surfactants, and mixtures thereof. The fluid treatment systems and compositions can be used to treat aqueous systems, for example as fracturing fluids for use in fracturing subterranean formations. Methods for inhibiting formation and/or precipitation of metal oxides in an aqueous composition using the fluid treatment systems or compositions also are provided.

Fluid treatment systems and compositions are provided including (a) at least one material including (1) at least one carboxylic acid functional group and (2) at least one sulfur-containing group selected from the group consisting of sulfonyl functional groups, sulfonate functional groups and mixtures thereof; and (b) at least one scale control agent. The fluid treatment systems and compositions can be used to treat aqueous systems, for example as fracturing fluids for treating aqueous compositions found in subterranean formations. Methods for inhibiting formation and/or precipitation of calcium salts in an aqueous composition using the fluid treatment systems or compositions also are provided.

The present invention provides a noble metal fine particle with a protein adsorbed thereon, including a noble metal fine particle, and a protein adsorbed on a surface of the noble metal fine particle. The protein has an isoelectric point in a range of pH 4.0 to 7.5. An amount of the protein adsorbed is in a range of 3 to 55.1 wt % with respect to a total weight of the noble metal fine particle and the protein. The noble metal fine particle with a protein adsorbed thereon according to the present invention has excellent redispersibility. That is, by adjusting the pH of a noble metal fine particle dispersed liquid to the isoelectric point of the proteins and allowing the noble metal fine particles to be aggregated without adding a degrading enzyme that degrades the proteins to the noble metal fine particle dispersed liquid, it is possible to allow the noble metal fine particles with proteins adsorbed thereon withdrawn from the noble metal fine particle dispersed liquid to have an average particle diameter that is not increased significantly even after they are redispersed in another dispersion medium.

Method, apparatus, and system for preparing a cellular material based on hollow metal beads. According to the description, at least one bead chain in which said hollow metal beads are linked to one another in pairs by means of an articulation is used as elementary structure constituting the cellular material.

The invention relates to a method for shaping a barrel spring made of a unitary ribbon of metallic glass that comprises calculating the theoretical shape to be given to said unitary ribbon of metallic glass so that each segment, once the spring is fitted in the barrel, is subjected to the maximum bending momentum, shaping said ribbon by imparting bends thereto characteristic of said free theoretical shape in order to take into account a potential reduction of the bends once the ribbon is released, relaxing the ribbon in order to set the shape thereof by heating the same, and cooling down said ribbon.

A power tool for installing a metal locking tie is disclosed. The power tool includes a body and a power chassis. The body of the tool includes a gear carrier, a tensioning mechanism and a cutting mechanism. The gear carrier is positioned in the tool body and the tensioning mechanism is mounted in the gear carrier. The cutting mechanism engages the gear carrier. As the tie is tensioned, the gear carrier moves linearly in the tool body to cut the tensioned tie.

A protective metal netting comprises a plurality of longitudinal metal wires or cables (10) side by side, each interwoven with at least one adjacent longitudinal wire or cable (10) in an interweave portion (24), in which at least one of the metal wires or cables (20) has an almost rectilinear development, or in any case with loops that are less pronounced than the lower-strength neighboring cables. A machine for manufacturing interwoven metal nettings comprises a cylindrical drum (50), on the outer surface of which a plurality of pins (52) protruding radially and arranged in axial rows at equal angular intervals is fixed, with an equal pitch in all the rows. Some pins (54) present on the cylindrical drum (50) are fitted out-of-alignment with respect to the above-mentioned pitch.

The present invention provides templating methods for replicating patterned metal films from a template substrate such as for use in plasmonic devices and metamaterials. Advantageously, the template substrate is reusable and can provide plural copies of the structure of the template substrate. Because high-quality substrates that are inherently smooth and flat are available, patterned metal films in accordance with the present invention can advantageously provide surfaces that replicate the surface characteristics of the template substrate both in the patterned regions and in the unpatterned regions.

A light-emitting element which emits light with high luminance and can be driven at low voltage. The light-emitting element includes n (n is a natural number of 2 or more) EL layers between an anode and a cathode, and includes a first layer, a second layer, and a third layer between an m-th (m is a natural number, 1≦m≦n−1) EL layer from the anode and an (m+1)th EL layer. The first layer functions as a charge-generation region, has hole-transport properties, and contains an acceptor substance. The third layer has electron-transport properties and contains an alkali metal or the like. The second layer formed of a metal complex having a metal-oxygen bond and an aromatic ligand is provided between the first and third layers, whereby an injection barrier at the time of injecting electrons generated in the first layer into the m-th EL layer through the third layer can be lowered.

A fireproof unit for a sliding closure at the spout of a container containing metal melt, including a fireproof adapter block that can be placed on the container spout, a fireproof bottom plate connected thereto, to which bottom plate a slidable fireproof sliding plate can be connected, wherein the sliding plate allows the sliding closure to be opened or closed. In addition to the first bottom plate connected to the adapter block, a second bottom plate adjoins the adapter block. The second bottom plate can be slid in under the adapter block to replace the first bottom plate. The adapter block has a length in the direction of the second bottom plate such that the adapter block is in sliding contact with the second bottom plate at the lower sliding surface of the adapter block.

The present invention relates to a process and apparatus for producing a fluid enriched in carbon dioxide starting from a waste gas from a ferrous metallurgy unit.

The invention relates to a metal-cutting machining process for a semi-finished product having a predetermined shape and at least one machining surface which has the steps: applying a protective foil having a predetermined elongation at break to the at least one machining surface with a predetermined adhesive force, placing a metal-cutting tool in a predetermined position above the machining surface, exerting a predetermined mechanical force in a predetermined direction for a predetermined length of time to the tool for carrying out a metal-cutting process on the semi-finished product and lifting the tool from the at least one machining surface after the predetermined length of time. In order to protect the semi-finished products from damage through the machining residues and at the same time not to impair the drilling performance, according to the invention through the adhesion an adhesive force is produced between the protective foil and the machining surface of substantially 10 N/25 mm and a protective foil is used which has an elongation at break of between 80 and 120%.

Disclosed is an improved pipe cutting tool based upon a ratchet closure action wherein handles are pivotedly attached to allow successive movement of a cutting blade in response to the squeezing of the handles. The handles are also hingedly coupled to the cutting member to maintain the cutting member in a position perpendicular to the tubular item to be cut while allowing the operator to squeeze the handles at offset angles, up to and including a right angle cut. The hinged handles allow for offset operation without forgoing the ease of operation by the consumer or causing a large reduction in the mechanical advantage. A ratchet allows sequential advancement of a cutting member toward a tubular shaped jaw that holds the item to be cut.

This disclosure generally relates to high-volume and cost-effective methods for producing non-spherical metal particles, particularly methods for producing metal cubes having rounded edges. The metal cubes having rounded edges are useful as ballistic shot in shotshell loads for hunting, where the particle shape imparted by the disclosed process packs to a higher density than spherical shot in the same volume.

Core-shell particles encapsulated by a thin film of a catalytically active metal are described. The particles are preferably nanoparticles comprising a non-noble core with a noble metal shell which preferably do not include Pt. The non-noble metal-noble metal core-shell nanoparticles are encapsulated by a catalytically active metal which is preferably Pt. The core-shell nanoparticles are preferably formed by prolonged elevated-temperature annealing of nanoparticle alloys in an inert environment. This causes the noble metal component to surface segregate and form an atomically thin shell. The Pt overlayer is formed by a process involving the underpotential deposition of a monolayer of a non-noble metal followed by immersion in a solution comprising a Pt salt. A thin Pt layer forms via the galvanic displacement of non-noble surface atoms by more noble Pt atoms in the salt. The overall process is a robust and cost-efficient method for forming Pt-coated non-noble metal-noble metal core-shell nanoparticles.

This invention relates to power metallurgical material, production method and application thereof. A metallurgy powder material with pressure-proof & good compactness, satisfactory to the component content requirements for 316 stainless steel, wherein, 5˜9% (by weight) of Fe3P (or Fe3PO4). The powder metallurgical material has properties of pressure resistance and corrosion resistance, and excellent compactness.

A pump for pumping molten metal and delivering flux includes a refractory base that can be submerged in molten metal including an impeller chamber, an inlet and an outlet. A refractory shaft sleeve has upper and lower end portions and is fastened to the base at the lower end portion. A motor is disposed near the upper end portion of the shaft sleeve. A refractory shaft extends in the shaft sleeve and is connected to the motor near the upper end portion of the shaft sleeve. A refractory impeller is connected to the shaft and is rotatable in the impeller chamber. A flux feeding device feeds flux into the shaft sleeve. Also featured is a method for delivering flux in the shaft sleeve of the pump and a method for cleaning flux accretions in the shaft sleeve.

A method of making metal nanoparticles and carbon nanotubes is disclosed. A mixture of a transition metal compound and an aromatic polymer, a precursor of an aromatic polymer, or an aromatic monomer is heated to form a metal nanoparticle composition, optionally containing carbon nanotubes.

The invention relates to a composition for synthesizing bimetallic nanoparticles, wherein the composition contains a first organometallic precursor and a second organometallic precursor having different decomposition rates and contained within an ionic liquid solution. The invention also relates to a method for synthesizing bimetallic nanoparticles, in which the composition is transformed under a hydrogen gas pressure between 0.1 and 10 MPa at a temperature between 0 and 150° C. until a suspension of bimetallic nanoparticles is obtained. The resulting nanoparticles are useful in diverse fields including the fields of catalysis and microelectronics.

The present invention provides a process for recovering valuable metals from precious metal smelting slag, comprising: smelting the precious metal smelting slag and a flux in a top-blown rotary furnace to produce a lead-bismuth alloy, wherein the precious metal smelting slag comprises Au, Ag, Bi and Pb; electrolyzing the lead-bismuth alloy at a current density ranging from 60 to 110 A/m2 to obtain lead cathode and lead anode slime; refining the lead anode slime to produce bismuth and silver-zinc crust, and extracting gold and silver separately from the silver-zinc crust. Through utilizing a top-blown rotary furnace as the smelting apparatus and adjusting the ratio of the flux, the present invention enriches the valuable metals gold, silver, bismuth, lead or the like to lead-bismuth alloy, ensures lower contents of gold, silver, bismuth and lead in the reducing slag and thereby increases the comprehensive recovery rates of gold, silver, bismuth and lead from the precious metal smelting slag.

A metal-bonded graphite foam composite includes a ductile metal continuous phase and a dispersed phase that includes graphite foam particles.

The invention relates to sputter targets and methods for depositing a layer from a sputter target. The method preferably includes the steps of: placing a sputter target in a vacuum chamber; placing a substrate having a substrate surface in the vacuum chamber; reducing the pressure in the vacuum chamber to about 100 Torr or less; removing atoms from the surface of the sputter target while the sputter target is in the vacuum chamber (e.g., using a magnetic field and/or an electric field). The deposited layer preferably is a molybdenum containing alloy including about 50 atomic percent or more molybdenum, 0.5 to 45 atomic percent of a second metal element selected from the group consisting of niobium and vanadium; and 0.5 to 45 atomic percent of a third metal element selected from the group consisting of tantalum, chromium, vanadium, niobium, and titanium.

Methods of forming metal matrix nanocomposites are provided. The methods include the steps of introducing a master metal matrix nanocomposite into a molten metal at a temperature above the melting temperature of the master metal matrix nanocomposite, allowing at least a portion of the master metal matrix nanocomposite to mix with the molten metal and, then, solidifying the molten metal to provide a second metal matrix nanocomposite.

The invention is directed to a process and apparatus for recovering metals from bottom ash from incineration plants, such as municipal waste incineration plants. The process includes directing a feed containing ash into an oxidizing unit, wherein at least part of the metals is oxidized in the presence of one or more acids and at least one oxygen donor, thus producing a stream comprising metal ions. From this stream the metals of interest are selected and converted into metallic form.

The present invention aims at improving a recovery rate of a positive-pole active substance and preventing a recovery loss of valuable metals when a positive-pole active substance is separated from a lithium ion battery. In the present invention, a material resulting from battery dismantling obtained by dismantling a lithium ion battery is stirred using a surfactant solution, whereby a positive-pole active substance is separated from a positive-electrode substrate. Also, it is preferable that an alkaline solution is added to a positive-electrode material of a material resulting from battery dismantling, thereby dissolving a positive-electrode substrate to which a positive-pole active substance adheres to obtain a slurry containing the positive-pole active substance, and a surfactant solution is added to the slurry to disperse the positive-pole active substance in the slurry, whereby the positive-pole active substance is separated from the alkaline solution.

A process for producing refractory metal alloy powders includes the steps of blending at least one powder with at least one solvent and at least one binder to form a slurry; forming a plurality of agglomerates from the slurry; screening the plurality of agglomerates; sintering the plurality of agglomerates; and melting said plurality of agglomerates to form a plurality of homogenous, densified powder particles.

Novel systems and methods are described for reducing iron oxide to metallic iron in an integrated steel mill or the like that has a coke oven and/or an oxygen steelmaking furnace. More specifically, the present invention relates to novel systems and methods for reducing iron oxide to metallic iron using coke oven gas (COG) or COG and basic oxygen furnace gas (BOFG).

A method for making a metal-based nano-composite material is disclosed. In the method, a semi-solid state metal-based material is provided. The semi-solid state metal-based material is stirred and nano-sized reinforcements are added into the semi-solid state metal-based material to obtain a semi-solid state mixture. The semi-solid state mixture is heated to a temperature above a liquidus temperature of the metal-based material, to achieve a liquid-metal-nano-sized reinforcement mixture. The liquid-metal-nano-sized reinforcement mixture is ultrasonically processed at a temperature above the liquidus temperature by conducting ultrasonic vibrations to the liquid-metal-nano-sized reinforcement mixture along different directions at the same time.

Carbothermic reduction of magnesium oxide at approximately 2200 degrees Kelvin yields a high temperature mixture of magnesium vapors and carbon monoxide gas. Previous processes have sought to cool or alter the mixture to cause the yield of pure magnesium, which is then used in subsequent processes for its reducing properties. The present invention takes advantage of the stability and inertness of carbon monoxide at elevated temperatures enabling the magnesium vapor/carbon monoxide gas mixture from the carbothermic process to be used directly for the production of other metals at high temperatures. Chromium oxide, manganese oxide, zinc oxide and sulfide, and several other metal compounds can be reduced by the magnesium vapor/carbon monoxide gas mixture at temperatures high enough to prevent the gas mixture from back-reacting to magnesium oxide and carbon.

The invention provides a recycling step in an oxidative pressure leaching process for recovery of metals using halide ions, in which a portion of the leached solids are recycled back to the feed to the autoclave, to allow two or more passes through the high temperature leaching step.

A metal material is contacted with a treatment solution containing zirconium and/or titanium compound, and a polyamine compound having a number average molecular weight from 150 to 500,000 and containing from 0.1 mmol to 17 mmol of primary and/or secondary amino group per 1 g of solid content and at least one siloxane unit. Concentration of zirconium and/or titanium compound in the metal surface treatment composition is from 10 ppm to 10,000 ppm with respect to the metal element, and mass ratio of the zirconium and/or titanium element is from 0.1 to 100 with respect to the polyamine compound. The metal material is washed with water after contacted by the treatment solution.

Provided a build-up welding material which contains C: 0.2 to 1.5 mass %, Si: 0.5 to 2 mass %, Mn: 0.5 to 2 mass %, Cr: 20 to 40 mass %, Mo: 2 to 6 mass %, Ni: 0.5 to 6 mass %, V: 1 to 5 mass % and W: 0.5 to 5 mass %, with the balance being Fe and unavoidable impurities.

Processes comprising: melting a mixture comprising a valve metal precursor and a diluting agent in at least one first vessel under a first set of temperature and residence time conditions; transferring the mixture to at least one second vessel; and initiating, in the at least one second vessel, a reaction of the valve metal precursor to form a valve metal under a second set of temperature and residence time conditions; valve metal powder prepared thereby and uses therefor.

A composition to decommission firearms is presented. The composition comprises a monomer, a quantity of calcium chloride; and sulfur-containing compound. The sulfur containing compound includes sodium persulfate and/or sodium thiosulfate.

A metal laminated substrate for an oxide superconducting wire is manufactured such that a non-magnetic metal plate T1 having a thickness of not more than 0.2 mm and a metal foil T2 made of Cu alloy which is formed by cold rolling at a draft of not less than 90% and has a thickness of not more than 50 μm is laminated to each other by room-temperature surface active bonding, after lamination, crystal of the metal foil is oriented by heat treatment at a temperature of not less than 150° C. and not more than 1000° C. and, thereafter, an epitaxial growth film T3 made of Ni or an Ni alloy having a thickness of not more than 10 μm is laminated to the metal foil.

Aqueous compositions useful as pretreatments prior to painting and to prevent the formation of white rust in the uncoated condition include an organopolyphosphonic acid or salt thereof, an organosilane, and a trivalent chromium compound. A method for treating a surface of a zinc-containing metal includes contacting the surface with an aqueous composition including an organopolyphosphonic acid or salt thereof, an organosilane, and a trivalent chromium compound. The composition may also include an agent for reducing hydrophilicity, such as a polyacrylic acid. The aqueous composition has been found to be particularly well-suited for treating a zinc-containing metal to passivate the surface, improve paint adhesion, and/or improve corrosion resistance.

A hand-operated implement has a guide bar on which is fitted a cutting chain for cutting mineral and metal materials. The cutting chain is driven around the guide bar by a chain sprocket. The chain sprocket is arranged in a chain sprocket chamber which is delimited by a chain sprocket cover. A cutting element has an outer side facing a sidewall of the chain sprocket cover which lies in a first notional plane. The distance between the sidewall and the first notional plane measured perpendicular to the first notional plane and centrally between the top of the cutting element and the peripheral wall is less than approximately 0.8 cm over at least 30% of the section between a second notional plane containing the central axis of a fixing bolt on the guide bar and the exit opening at which the cutting chain leaves the chain sprocket chamber.

An arrangement for a continuous casting process. The arrangement includes a vessel having a first opening for receiving molten metal in the vessel, a second opening for discharging the molten metal from the vessel, and a body extending between the first opening and the second opening, a first magnetic arrangement attached to the body, the first magnetic arrangement having a magnetic core with legs, and coils arranged around the legs, and a power system configured to provide an alternating current superimposed on a carrier current to each of the coils, each pair of alternating current and carrier current provided to a coil forming a flow control current, wherein flow control currents provided to adjacent coils are phase shifted relative each other, thereby creating a travelling magnetic field in molten metal in the vessel. A corresponding method is also presented herein.

Metal alloy injection molding techniques are described. In one or more implementations, these techniques may also include adjustment of injection pressure, configuration of runners, and/or use of vacuum pressure, and so on to encourage flow of the metal alloy through a mold. Techniques are also described that utilize protrusions to counteract thermal expansion and subsequent contraction of the metal alloy upon cooling. Further, techniques are described in which a radius of edges of a feature is configured to encourage flow and reduce voids. A variety of other techniques are also described herein.

Provided herein are various embodiments of systems for casting thin metal plates and sheets. Typical embodiments include layers of mold cavities that are oriented vertically for casting the metal plates. In some embodiments, the mold cavities include a beveled edge such that the plates that are cast have a beveled edge. In some embodiments, the mold cavities are filled with a molten metal through an open horizontal edge of the cavity. In some embodiments, the mold cavities are filled through one or more vertical feed orifices. Further disclosed are methods for forming a thin cast metal plate or sheet where the thickness of the cast part is in a range from 0.005 inches to 0.2 inches, and the surface area of the cast part is in a range from 16 square inches to 144 square inches.

A new method for continuous casting of molten metal is provided that allows one to obtain an intermediate product such as slab, billet wire, etc. before subsequent thermomechanical treatment (e.g. lamination or annealing), such that its chemical composition is modified by the addition of elements in order to give it greater mechanical strength.

A non-electroslag remelting type clean metal ingot mold includes an ingot mold body and a insulating riser arranged on the ingot mold body; an insulated heating and heat preservation device is vertically arranged in the ingot mold body and divides the space in the ingot mold body into a plurality of independent cavity units; and the cavity units are distributed in two rows in the ingot mold body. Because the insulated heating and heat preservation device is arranged in the ingot mold body and divides the space in the ingot mold body into a plurality of independent cavity units, most of impurities and segregates in liquid metals are enriched in the part in contact with the isolation and heat insulation mechanism during the directional solidification and crystallization of the liquid metals and the enriched alloy segregates, and the impurities can be easily eliminated by utilizing flame or other processing methods.

A clean metal ingot mold comprises an ingot mold body and an insulating riser arranged on the ingot mold body. The bottom mold plate of the ingot mold is provided with at least a ridge connected thereto. The region having a V-shape containing impurities produced during the crystallization process of the liquid metal moves upwards because of the ridge, and then the impurities depart from the center of the cast ingot and the impurities are more centralized. A water-cooling device is arranged in the ridge to allow the temperature of the metal in the ingot mold to decrease rapidly, and the crystallization process of the metal to be rapid.

A method for manufacturing a thin metal strip by pouring and rapidly solidifying molten metal onto a cooling roll rotating at a high speed to form a thin metal strip having a width of 50˜350 mm, blowing compression gas from substantially a tangential direction of the cooling roll toward the thin metal strip to separate the thin metal strip from the cooling roll, adsorbing the separated thin metal strip with a permeable belt of a suction type belt conveyor, and transporting to a take-up reel to wind in form of a coil, the thin metal strip is adsorbed by the belt under conditions that a nearest approaching distance L between the cooling roll and the suction type belt conveyor is 2˜50 mm and a suction width S of a suction box arranged in the suction type belt conveyor is 1.2˜2.5 times of a width W of the thin metal strip.

Provided in one embodiment is a method of forming a connection mechanism in or on a bulk-solidifying amorphous alloy by casting in or on, or forming with the bulk-solidifying amorphous alloy, a machinable metal. The connection mechanism can be formed by machining the machinable metal.