Single crystals of the inter­metallic phase with composition Ti4Ni2C were serendipitously obtained by high-pressure sinter­ing of a mixture with initial chemical composition Ti2Ni. The Ti4Ni2C phase crystallizes in the Fdoverline{3}m space group and can be considered as a partially filled Ti2Ni structure with the C atom occupying an octa­hedral void. Ti4Ni2C is isotypic with Ti4Ni2O, Nb4Ni2C and Ta4Ni2C, all of which were studied previously by means of powder diffraction.

The phase with composition Ti4Fe2C0.82O0.18, tetra­titanium diiron carbide oxide, was unexpectedly synthesized by high-pressure sinter­ing (HPS) of a stoichiometric mixture with nominal composition Ti2Fe. The Ti4Fe2C0.82O0.18 phase crystallizes in the Fdoverline{3}m space group and can be considered as the Ti2Fe structure filled with C and O atoms co-occupying the same octa­hedral void [occupancy ratio 0.82 (7):0.18 (7)]. The Ti4Fe2C0.82O0.18 phase is isotypic with Ti4Ni2C and Ti4Fe2O0.407, and is the first example where C and O atoms co-occupy the same site in filled Ti2Fe structures.