A high strength, corrosion resistant alloy suitable for use in oil and gas environments includes, in weight %: 0-12% Fe, 18-24% Cr, 3-6.2% Mo, 0.05-3.0% Cu, 4.0-6.5% Nb, 1.1-2.2% Ti, 0.05-0.4% 0.05-0.2% Al, 0.005-0.040% C, balance Ni plus incidental impurities and deoxidizers. A ratio of Nb/(Ti+Al) is equal to 2.5-7.5 to provide a desired volume fraction of γ' and γ″ phases. The alloy has a minimum yield strength of 145 ksi.

A hot-forged copper alloy part which has a tubular shape, in which an alloy composition contains 59.0 mass % to 84.0 mass % of Cu and 0.003 mass % to 0.3 mass % of Pb with a remainder of Zn and inevitable impurities, a content of Cu [Cu] mass % and a content of Pb [Pb] mass % have a relationship of 59≦([Cu]+0.5×[Pb])≦64, a shape of the forged part satisfies a formula of 0.4≦(average inner diameter)/(average outer diameter)≦0.92, 0.04≦(average thickness)/(average outer diameter)≦0.3, and 1≦(tube axis direction length)/(average thickness))≦10, a forging material which is to be hot-forged has a tubular shape and satisfies 0.3≦(average inner diameter/average outer diameter)≦0.88, 0.06≦(average thickness)/(average outer diameter)≦0.35, and 0.8≦(tube axis direction length)/(average thickness))≦12, and 0%≦(degree of uneven thickness)≦30%, 0≦(degree of uneven thickness)≦75×1/((tube axis direction length)/(average thickness))1/2 in any location in a tube axis direction.

The present invention provides ultralow carbon thin gauge steel sheet and a method for producing the same where coalescence and growth of inclusions in the molten steel are prevented and the inclusions are finely dispersed in the steel sheet, whereby surface defects and cracks at the time of press forming are prevented, growth of recrystallized grains at the time of continuous annealing is promoted, and a high r value (r value≧2.0) and elongation (total elongation≧50%) are exhibited, that is, ultralow carbon thin gauge steel sheet excellent in surface conditions, formability, and workability comprised of, by mass %, 0.00030.003%≦C≦0.003%, Si≦0.01%, Mn≦0.1%, P≦0.02%, S≦0.01%, 0.0005%≦N≦0.0025%, 0.01%≦acid soluble Ti≦0.07%, acid soluble Al≦0.003%, and 0.002%≦La+Ce+Nd≦0.02% and a balance of iron and unavoidable impurities, said steel sheet characterized by containing at least cerium oxysulfite, lanthanum oxysulfite, and neodymium oxysulfite.

[Object] To provide a method of manufacturing a sputtering target and a sputtering target that are capable of achieving refinement and uniformity of crystal grains. [Solving Means] A method of manufacturing a sputtering target according to an embodiment of the present invention includes forging an ingot formed of metal by applying a stress in a first axis direction (z-axis direction) and a plane direction (xy-plane direction) orthogonal to the first axis direction. The ingot is additionally forged by applying a stress in a second axis direction (axial directions c11, c12, c21, c22) obliquely intersecting with a direction parallel to the first axis direction. The ingot is heat-treated at a temperature equal to or higher than a recrystallization temperature thereof. In such a manner, since slip deformation can be caused not only in the first axis direction and the plane direction orthogonal thereto but also in the second axis direction, the high density and uniformity of an internal stress can be achieved.

A high-strength seamless steel pipe for oil wells excellent in sulfide stress cracking resistance which comprises, on the percent by mass basis, C: 0.1 to 0.20%, Si: 0.05 to 1.0%, Mn: 0.05 to 1.0%, Cr: 0.05 to 1.5%, Mo: 0.05 to 1.0%, Al: 0.10% or less, Ti: 0.002 to 0.05% and B: 0.0003 to 0.005%, with a value of equation “C+(Mn/6)+(Cr/5)+(Mo/3)” of 0.43 or more, with the balance being Fe and impurities, and in the impurities P: 0.025% or less, S: 0.010% or less and N: 0.007% or less. The seamless steel pipe may contain a specified amount of one or more element(s) of V and Nb, and/or a specified amount of one or more element(s) of Ca, Mg and REM. The seamless steel pipe can be produced at a low cost by adapting an in-line tube making and heat treatment process having a high production efficiency since a reheating treatment for refinement of grains is not required.

In various embodiments, planar sputtering targets are produced by forming a billet at least by pressing molybdenum powder in a mold and sintering the pressed powder, working the billet to form a worked billet, heat treating the worked billet, working the worked billet to form a final billet, and heat treating the final billet.

A method of forming a wrought material having a refined grain structure is provided. The method comprises providing a metal alloy material having a depressed solidus temperature and a low temperature eutectic phase transformation. The metal alloy material is molded and rapidly solidified to form a fine grain precursor that has fine grains surrounded by a eutectic phase with fine dendritic arm spacing. The fine grain precursor is plastic deformed at a high strain rate to cause recrystallization without substantial shear banding to form a fine grain structural wrought form. The wrought form is then thermally treated to precipitate the eutectic phase into nanometer sized dispersoids within the fine grains and grain boundaries and to define a thermally treated fine grain structure wrought form having grains finer than the fine grains and the fine dendritic arm spacing of the fine grain precursor.

An annealing process for a TMR or GMR sensor having an amorphous free layer is disclosed and employs at least two annealing steps. A first anneal at a temperature T1 of 200° C. to 270° C. and for a t1 of 0.5 to 15 hours is employed to develop the pinning in the AFM and pinned layers. A second anneal at a temperature T2 of 260° C. to 400° C. where T2>T1 and t1>t2 is used to crystallize the amorphous free layer and complete the pinning. An applied magnetic field of about 8000 Oe is used during both anneal steps. The mechanism for forming a sensor with high MR and robust pinning may involve structural change in the tunnel barrier or at an interface between two of the layers in the spin valve stack. A MgO tunnel barrier and a CoFe/CoB free layer are preferred.

A steel material superior in high temperature characteristics and toughness is provided, that is, a steel material containing, by mass %, C: 0.005% to 0.03%, Si: 0.05% to 0.40%, Mn: 0.40% to 1.70%, Nb: 0.02% to 0.25%, Ti: 0.005% to 0.025%, N: 0.0008% to 0.0045%, B: 0.0003% to 0.0030%, restricting P: 0.030% or less, S: 0.020% or less, Al: 0.03% or less, and having a balance of Fe and unavoidable impurities, where the contents of C and Nb satisfy C—Nb/7.74≦0.02 and Ti-based oxides of a grain size of 0.05 to 10 μm are present in a density of 30 to 300/mm2.

A steel for heat treatment, which exhibits high strength and high toughness even when the heat treatment (such as quenching and tempering) of the steel is conducted under conventional conditions in an after stage. The steel for heat treatment contains C: 0.10 to 0.70 mass %, Mn: 0.1 to 3.0 mass %, Al: 0.005 to 2.0 mass %, P: 0.050 mass % or less, S: 0.50 mass % or less, O: 0.0030 mass or less, N: 0.0200 mass % or less, and one or more selected from the group consisting of Ti: 0.30 mass % or less and Nb: 0.30 mass or less with the balance being Fe and unavoidable impurities, and has a TH value of 1.0 or above as calculated according to the formula: ({Ti}/48+{Nb}/93) 104 and grain diameters of 10 μm or below. {Ti} and {Nb} refer respectively to the contents of Ti and Nb in precipitates of 5 to 100 nm in size as determined about their respective extraction residues.

Provided is a NdFeB sintered magnet which can be used in the grain boundary diffusion method as a base material in which RH can be easily diffused through the rare-earth rich phase and which itself has a high coercive force, a high maximum energy product and a high squareness ratio, as well as a method for producing such a magnet. A NdFeB system sintered has an average grain size of the main-phase grains magnet is equal to or smaller than 4.5 μm, the carbon content of the entire NdFeB system sintered magnet is equal to or lower than 1000 ppm, and the percentage of the total volume of a carbon rich phase in a rare-earth rich phase at a grain-boundary triple point in the NdFeB system sintered magnet to the total volume of the rare-earth rich phase is equal to or lower than 50%.

The present invention provides a high Al-content steel sheet having an excellent workability and a method of production of the same at a low cost by mass production, a high Al-content metal foil and a method of production of the same, and a metal substrate using a high Al-content metal foil, that is, a high Al-content steel sheet having an Al content of 6.5 mass % to 10 mass %, the high Al-content steel sheet characterized by having one or both of a {222} plane integration of an α-Fe crystal with respect to the surface of the steel sheet of 60% to 95% or a {200} plane integration of 0.01% to 15% and a method of production of the same, a high Al-content metal foil and a method of production of the same, and a metal substrate using a high Al-content metal foil.

A method of manufacturing a high-strength galvanized steel sheet includes hot-rolling a slab to form a steel sheet; during continuous annealing, heating the steel sheet to a temperature of 750° C. to 900° C. at an average heating rate of at least 10° C./s at a temperature of 500° C. to an A1 transformation point; holding that temperature for at least 10 seconds; cooling the steel sheet from 750° C. to a temperature of (Ms point—100° C.) to (Ms point—200° C.) at an average cooling rate of at least 10° C./s; reheating the steel sheet to a temperature of 350° C. to 600° C.; holding that temperature for 10 to 600 seconds; and galvanizing the steel sheet.

A method for treating a component comprising a metallic or ceramic material with a crystalline, semi-crystalline or amorphous structure. According to the method, to case-harden the component, at least part of the surface of the component is exposed to an oil jet, while the temperature of the oil and/or the component is regulated. Also disclosed is a device for carrying out the method.

A metal material is contacted with a treatment solution containing zirconium and/or titanium compound, and a polyamine compound having a number average molecular weight from 150 to 500,000 and containing from 0.1 mmol to 17 mmol of primary and/or secondary amino group per 1 g of solid content and at least one siloxane unit. Concentration of zirconium and/or titanium compound in the metal surface treatment composition is from 10 ppm to 10,000 ppm with respect to the metal element, and mass ratio of the zirconium and/or titanium element is from 0.1 to 100 with respect to the polyamine compound. The metal material is washed with water after contacted by the treatment solution.

Embodiments of the present invention provide apparatus and methods for performing rapid thermal processing. One embodiment of the present invention provides an apparatus for processing a substrate. The apparatus includes a heating source disposed outside a chamber body and configured to provide thermal energy towards a processing volume. The substrate support defines a substrate supporting plane, and the substrate support is configured to support the substrate in the substrate supporting plane. The heating source includes a frame member having an inner wall surrounding an area large enough to encompass a surface area of the substrate, and a plurality of diode laser tiles mounted on the inner wall of the frame member. Each of the plurality of diode laser tiles is directed towards a corresponding area in the processing volume.

Processes comprising: melting a mixture comprising a valve metal precursor and a diluting agent in at least one first vessel under a first set of temperature and residence time conditions; transferring the mixture to at least one second vessel; and initiating, in the at least one second vessel, a reaction of the valve metal precursor to form a valve metal under a second set of temperature and residence time conditions; valve metal powder prepared thereby and uses therefor.

A manufacturing method for a composite steel part including manufacturing a first steel part by preparing an intermediate product in which an extra portion is added, and heating the intermediate product to an austenitizing temperature in a carburizing atmosphere to form a carburized layer, cooling the intermediate product at a rate less than a cooling rate at which martensitic transformation is caused and in which the intermediate product is cooled to a temperature equal to or less than a temperature at which structure transformation due to the cooling is completed, heating the intermediate product to an austenitizing range by high-density energy and thereafter cooled at a rate equal to or more than the cooling rate at which martensitic transformation is caused to form a carburized quenched portion, cutting the extra portion of the intermediate product, and welding the first steel part and the second steel part to each other.

A composition to decommission firearms is presented. The composition comprises a monomer, a quantity of calcium chloride; and sulfur-containing compound. The sulfur containing compound includes sodium persulfate and/or sodium thiosulfate.

A method for manufacturing a hot-rolled sheet attains grain refinement of the steel sheet whose grain size is extremely fine. In particular, a ferrite grain size of less than average 2 μm is obtained, which is not laminar but has ferrite grains with equiaxed morphology and exhibits high formability in forming. The method comprises the steps of rolling and cooling, wherein the rolling reductions, cooling steps, and temperature are closely regulated. A hot rolled sheet made from the method of manufacturing has a controlled ferrite grain in different regions of sheet thickness.

A component composition contains, by % by mass, 0.0016 to 0.01% of C, 0.05 to 0.60% of Mn, and 0.020 to 0.080% of Nb so that the C and Nb contents satisfy the expression, 0.4≦(Nb/C)×(12/93)≦2.5. In addition, the amount of Nb-based precipitates is 20 to 500 ppm by mass, the average grain diameter of the Nb-based precipitates is 10 to 100 nm, and the average crystal grain diameter of ferrite is 6 to 10 μm. Nb is added to ultra-low-carbon steel used as a base, and the amount and grain diameter of the Nb-based precipitates are controlled to optimize the pinning effect. Grain refinement of ferrite is achieved by specifying the Mn amount, thereby achieving softening and excellent resistance to surface roughness of steel.

Provided is bearing steel excellent in workability after spheroidizing-annealing and in hydrogen fatigue resistance property after quenching and tempering. The bearing steel has a chemical composition containing, by mass %: 0.85% to 1.10% C; 0.30% to 0.80% Si; 0.90% to 2.00% Mn; 0.025% or less P; 0.02% or less S; 0.05% or less Al; 1.8% to 2.5% Cr; 0.15% to 0.4% Mo; 0.0080% or less N; and 0.0020% or less O, which further contains more than 0.0015% to 0.0050% or less Sb, with the balance being Fe and incidental impurities, to thereby effectively suppress the generation of WEA even in environment where hydrogen penetrates into the steel, so as to improve the roiling contact fatigue life and also the workability such as cuttability and forgeability of the material.

A low alloy steel ingot contains from 0.15 to 0.30% of C, from 0.03 to 0.2% of Si, from 0.5 to 2.0% of Mn, from 0.1 to 1.3% of Ni, from 1.5 to 3.5% of Cr, from 0.1 to 1.0% of Mo, and more than 0.15 to 0.35% of V, and optionally Ni, with a balance being Fe and unavoidable impurities. Performing quality heat treatment including a quenching step and a tempering step to the low alloy steel ingot to obtain a material, which has a grain size number of from 3 to 7 and is free from pro-eutectoid ferrite in a metallographic structure thereof, and which has a tensile strength of from 760 to 860 MPa and a fracture appearance transition temperature of not higher than 40° C.

This invention provides a copper alloy sheet material containing, in mass %, Ni: 0.7%-4.2% and Si: 0.2%-1.0%, optionally containing one or more of Sn: 1.2% or less, Zn: 2.0% or less, Mg: 1.0% or less, Co: 2.0% or less, and Fe: 1.0% or less, and a total of 3% or less of one or more of Cr, B, P, Zr, Ti, Mn and V, the balance being substantially Cu, and having a crystal orientation satisfying Expression (1): I{420}/I0{420}>1.0 (1), where I{420} is the x-ray diffraction intensity from the {420} crystal plane in the sheet plane of the copper alloy sheet material and I0{420} is the x-ray diffraction intensity from the {420} crystal plane of standard pure copper powder. The copper alloy sheet material has highly improved strength, post-notching bending workability, and stress relaxation resistance property.

A metal laminated substrate for an oxide superconducting wire is manufactured such that a non-magnetic metal plate T1 having a thickness of not more than 0.2 mm and a metal foil T2 made of Cu alloy which is formed by cold rolling at a draft of not less than 90% and has a thickness of not more than 50 μm is laminated to each other by room-temperature surface active bonding, after lamination, crystal of the metal foil is oriented by heat treatment at a temperature of not less than 150° C. and not more than 1000° C. and, thereafter, an epitaxial growth film T3 made of Ni or an Ni alloy having a thickness of not more than 10 μm is laminated to the metal foil.

A cobalt-nickel base alloy is disclosed. The alloy includes, in weight percent: greater than about 4 % of Al, about 10 to about 20 % of W, about 10 to about 40 % Ni, about 5 to 20 % Cr and the balance Co and incidental impurities. The alloy has a microstructure that is substantially free of a CoAl phase having a B2 crystal structure and configured to form a continuous, adherent aluminum oxide layer on an alloy surface upon exposure to a high-temperature oxidizing environment. A method of making an article of the alloy includes: selecting the alloy; forming an article from the alloy; solution-treating the alloy; and aging the alloy to form an alloy microstructure that is substantially free of a CoAl phase having a B2 crystal structure, wherein the alloy is configured to form a continuous, adherent aluminum oxide layer on an alloy surface upon exposure to a high-temperature oxidizing environment.

A welding method for welding workpieces made of highly heat-resistant superalloys is provided. The method includes generating a heat input zone on the workpiece surface by means of a heat source, feeding welding filler material into the heat input zone by means of a feeding device, and generating a relative motion between the heat source and the feeding device on one hand and the workpiece surface on the other hand by means of a conveying device. Furthermore, according to the welding method, the mass feed rate is ≦350 mg/min.

The present invention relates to methods and compositions for coating aluminum substrates. In an embodiment, the invention includes a method of applying a coating on an aluminum substrate including contacting the aluminum substrate with a first solution. The first solution can include a zinc metal salt, a sugar acid or alkali metal salt thereof, and an alkali metal hydroxide. The method can also include contacting the aluminum substrate with a second solution. The second solution can include a molybdate salt, an alkanolamine, and a fluorine acid. Other embodiments are also included herein.

Aqueous compositions useful as pretreatments prior to painting and to prevent the formation of white rust in the uncoated condition include an organopolyphosphonic acid or salt thereof, an organosilane, and a trivalent chromium compound. A method for treating a surface of a zinc-containing metal includes contacting the surface with an aqueous composition including an organopolyphosphonic acid or salt thereof, an organosilane, and a trivalent chromium compound. The composition may also include an agent for reducing hydrophilicity, such as a polyacrylic acid. The aqueous composition has been found to be particularly well-suited for treating a zinc-containing metal to passivate the surface, improve paint adhesion, and/or improve corrosion resistance.

The invention concerns a cold-rolled aluminum killed steel sheet, which includes by weight between 0.003 and 0.130% of carbon, between 0.10 and 1% of manganese, between 0.010 and 0.100% of aluminum, between 0.0015 and 0.0140% nitrogen, the remainder being of iron and impurities resulting from the manufacturing, and which has a content of carbon in solid solution (Css) of at least 50 ppm, as well as a method of manufacturing packaging from said sheet.

A multiphase steel sheet has a steel composition containing, in percent by mass, more than 0.015% to less than 0.100% of carbon, less than 0.40% of silicon, 1.0% to 1.9% of manganese, more than 0.015% to 0.05% of phosphorus, 0.03% or less of sulfur, 0.01% to 0.3% of soluble aluminum, 0.005% or less of nitrogen, less than 0.30% of chromium, 0.0050% or less of boron, less than 0.15% of molybdenum, 0.4% or less of vanadium, 0.02% or less of titanium, wherein [Mneq] is 2.0 to 2.8, the balance being iron and incidental impurities.

An aluminum alloy wrought product including, in wt. %, Mg 3.0 to 7.0, Zn 0.6 to 2.8, Mn 0 to 1.0, Cu 0 to 2.0, Sc 0 to 0.6, at least one element selected from the group of Zr 0.04 to 0.4, Cr 0.04 to 0.4, Hf 0.04 to 0.4 and Ti 0.01 to 0.3; Fe maximum 0.3, Si maximum 0.3, inevitable impurities, and balance aluminum. The range for the Zn-content in wt. % is a function of the Mg-content according to: lower-limit of the Zn-range: [Zn]=0.34[Mg]−0.4, and upper-limit of the Zn-range: [Zn]=0.34[Mg]+0.4.

Provided is a method of preparing a nanocrystalline titanium alloy at low strain to have better strength. The present invention is characterized in that an initial microstructure is induced as martensites having a fine layered structure, and then a nanocrystalline titanium alloy is prepared at low strain by optimizing process variables through observation of the effects of strain, strain rate, and deformation temperature on the changes in the microstructure.

An aluminum alloy forging material of the present invention is constituted by an aluminum alloy cast product obtained by subjecting an aluminum alloy ingot having a structure in which a secondary dentrite arm spacing (DAS) is 40 μm or less and an average grain diameter of crystallized substances is 8 μm or less to homogenization treatment for holding the ingot for one hour or more under temperature conditions of 450 to 510° C., wherein the ingot is obtained by continuously casting a molten aluminum alloy having an alloy composition consisting of: Si: 0.80 to 1.15 mass %; Fe: 0.2 to 0.5 mass %; Cu: 3.8 to 5 mass %; Mn: 0.8 to 1.15 mass %; Mg: 0.5 to 0.8 mass %; Zr: 0.05 to 0.13 mass %; and Ti contained in such an amount that a sum of Ti and Zr is 0.2 mass % or less, and the balance being Al and inevitable impurities, wherein the alloy composition satisfies a Cu/Mg ratio of 8 or less, Ti is added in a form of an Al master alloy (5Ti-1B mother alloy) in which Ti and B are contained at a ratio of 5:1, and a Ti/Zr ratio satisfies 0.3 or higher.

There are provided a permanent magnet and a manufacturing method thereof enabling carbon content contained in magnet particles to be reduced in advance before sintering even when wet milling is employed. Coarsely-milled magnet powder is further milled by a bead mill in a solvent together with an organometallic compound expressed with a structural formula of M-(OR)X (M represents V, Mo, Zr, Ta Ti W or Nb, R represents a substituent group consisting of a straight-chain or branched-chain hydrocarbon, X represents an arbitrary integer) so as to uniformly adhere the organometallic compound to particle surfaces of the magnet powder. Thereafter, a compact body of compacted magnet powder is held for several hours in hydrogen atmosphere at 200 through 900 degrees Celsius to perform hydrogen calcination process. Thereafter, through sintering process, a permanent magnet 1 is formed.

A steel for an induction hardening including, by mass %, C: more than 0.75% to 1.20%, Si: 0.002 to 3.00%, Mn: 0.20 to 2.00%, S: 0.002 to 0.100%, Al: more than 0.050% to 3.00%, P: limited to 0.050% or less, N: limited to 0.0200% or less, O: limited to: 0.0030% or less, and the balance composing of iron and unavoidable impurities, wherein an Al content and a N content satisfy, by mass %, Al−(27/14)×N>0.050%.

The galvannealed steel sheet includes: a galvannealed layer formed on at least one surface of a steel sheet and contains includes an amount of 0.05 mass % to 0.5 mass % of Al, an amount of 6 mass % of 12 mass % of Fe, and the balance composed of Zn and inevitable impurities; and a mixed layer formed on a surface of the galvannealed layer and includes a composite oxide of Mn, Zn, and P and an aqueous P compound, wherein the composite oxide includes 0.1 mg/m2 to 100 mg/m2 of Mn, an amount of 1 mg/m2 to 100 mg/m2 of P, and Zn, and a P/Mn ratio is 0.3 to 50, and wherein the total size of an area of the mixed layer in which an attached amount of P is equal to or more than 20 mg/m2 is 20% to 80% of a surface area of the mixed layer.

Apparatus and method are provided for making the longitudinal temperature distribution of the bulbous end of a longitudinally oriented workpiece, such as a rail's head, generally uniform when the head has a non-uniform longitudinal temperature distribution. A combination of crown and skirt electric inductors is used to achieve the generally uniform temperature distribution by modulating the magnetic field intensity produced by current flow through one or more of the combination of crown and skirt inductors as required for the non-uniformly heated regions of the rail's head.

In one aspect, a method is disclosed that includes providing a substrate having a topography that comprises a relief and providing an anti-reflective film conformally over the substrate using a molecular layer deposition step. The anti-reflective film may be formed of a compound selected from the group consisting of: (i) an organic compound chemically bound to an inorganic compound, where one of the organic compound and the inorganic compound is bound to the substrate and where the organic compound absorbs light at at least one wavelength selected in the range 150-500 nm, or (ii) a monodisperse organic compound absorbing light at at least one wavelength selected in the range 150-500 nm. The method further includes providing a photoresist layer on the anti-reflective film.

Provided is a hot-rolled steel sheet that has a chemical composition including, by mass %: C: 0.060% to 0.150%; Si: 0.15% to 0.70%; Mn: 1.00% to 1.90%; P: 0.10% or less; S: 0.010% or less; Al: 0.01% to 0.10%; N: 0.010% or less; Nb: 0.010% to 0.100%; and the balance including Fe and incidental impurities. The hot-rolled steel sheet has a microstructure containing ferrite of 18 μm or less in average grain size by a volume fraction of at least 75% and pearlite of at least 2 μm in average grain size by a volume fraction of at least 5%, the balance being low-temperature-induced phases, the pearlite having a mean free path of at least 5.0 μm.

A predetermined steel containing Te: 0.0005 mass % to 0.0050 mass % is heated to 1320° C. or lower to be subjected to hot rolling, and is subjected to annealing, cold rolling, decarburization annealing, and nitridation annealing, and thereby a decarburized nitrided steel sheet is obtained. Further, an annealing separating agent is applied on the surface of the decarburized nitrided steel sheet and finish annealing is performed, and thereby a glass coating film is formed. The N content of the decarburized nitrided steel sheet is set to 0.0150 mass % to 0.0250 mass % and the relationship of 2×[Te]+[N]≦0.0300 mass % is set to be established. Note that [Te] represents the Te content and [N] represents the N content.

A biometric monitoring device and multiple carrying cases for same are provided. In some implementations, the case may be made from a flexible viscoelastic material and the biometric monitoring device may be slipped into a receptacle in the case through an opening in the case; the opening may become distended during the insertion of the biometric monitoring device. In some implementations, the case may feature a display window that, in combination with materials of the biometric monitoring device, may mask a display of the biometric monitoring device from view when the display is off and may allow the display to be seen when the display is displaying content.

A multipurpose organizer that can be quickly and easily converted into multiple articles such as but not limited to a carrying tote, a purse, a seat organizer and a head rest is provided. The method of making the multifunctional organizer and the methods of using the multifunctional organizer are also provided. In one embodiment the main body of consists of a single piece of material providing for low cost construction.

A system and a device for anti-thief protection, especially for open pockets of trousers, bags and the like, includes a mobile protection strip element (1) to be applied on the pockets hooks (12). The aim is attained by superposing the strip (1) on the pocket (T) and blocking the strip (1) using a plurality of hooks (12) in the form of clips located in the lower part (5) of the strip (1), the strip (1) supported by support elements (G), located in the upper part (2) thereof, which insert or hook in the zone overlying the pocket (T) to be protected.

A reusable flexible sheet for wrapping an object is presented. The flexible sheet includes a center portion having a first side, a second side, a third side, and a fourth side, the first side being parallel to the third side and the second side being parallel to the fourth side. Flaps are connected to the first side and the third side, and bow portions are connected to the second side and the fourth side. The bow portions tie together to form a decorative bow.

Embodiments of club head covers having a pull strap and methods to manufacture club head covers are generally described herein. Other embodiments of club head covers having a pull strap may be described and claimed.

A reusable gift wrap and a method of wrapping a gift comprising a sheet of material and a fastener. The sheet has a plurality of corners. The fastener comprises a body fabricated from a resilient material and is attached near one of the corners. A plurality of coterminous radially extending slits are formed in a face of the body and define the edges of a plurality of pivotable flaps and an opening for receiving the other corners of the sheet. The flaps comprises a living hinge which permit each of the flaps to pivot. The flaps increase in thickness from the living hinge to the edge of the flap. The three flaps simulate the appearance of a cuboidal gift box.

A smart card with an RFID tag is held in a wallet comprising a back layer and at least one front layer stitched to the back layer around part of a perimeter thereof to define at least one pocket in the wallet dimensioned to hold and completely surround the smart card. Both of the layers are composed of a stainless steel fabric capable of blocking RF radiation.

Disclosed is a digital frame cover comprised of two basic components which are utilized in conjunction with each other to decorate the front perimeter of a digital frame. The two primary components of the digital frame cover being (1) a hollow rectangular cover comprising cutouts at various locations, and (2) a “decorative wrap” of interior dimensions which allow the decorative wrap to fit snugly over the exterior of the cover. The cover slides/snaps onto the digital frame. The decorative wrap adheres to, or is magnetically attached to the cover. At the user's prerogative, the decorative wrap may be configured to display one or more of a selection of user-selected designs (i.e., wording, pictures, or appliqués).

A head cover for a golf club includes a first surface having a removable cleaning pad thereon, and a second surface on which at least one golf accessory constructed of a ferrous metal is removably attached thereto. The second surface is part of a tri-layer construction with magnets forming the second middle layer so as to so retain the golf accessory thereon. The cleaning pad is removed by the golfer from the first surface and includes a scrubbing area to remove grit and/or debris from one of a golf ball and a golf club face.